Product |
MgO (%) in DBM |
Fixed C (%) |
A.P (%) |
Coked A.P (%) at 1000°C in reducing atmosphere |
B.D (gm/cm3) |
C.C.S
(kg/cm2) |
M.O.R (kg/cm2)at room temperature |
M.O.R (kg/cm2) at 1400°C |
Primary Raw Material |
Application area |
VRPL MAGCARB-SL10 |
97.5 |
8.0 |
5 |
12 |
3.00 |
500 |
125 |
110 |
Fused Magnesia(crystal size:450-600 microns)and Graphite |
EBT / EOF, LD Converter |
VRPL MAGCARB-SL15 |
97.5 |
13.0 |
6 |
13 |
2.98 |
500 |
125 |
110 |
Fused Magnesia(crystal size:450-600 microns) and Graphite |
VRPL MAGCARB-HS10 |
97.5 |
8.0 |
5 |
12 |
3.00 |
500 |
125 |
110 |
Fused Magnesia (crystal size:450-600 microns) and Graphite |
VRPL MAGCARB-HS15 |
97.5 |
13.0 |
6 |
13 |
2.98 |
500 |
125 |
110 |
Fused Magnesia (crystal size:450-600 microns) and Graphite |
VRPL MAGCARB-HS20 |
97.5 |
18.0 |
6 |
14 |
2.95 |
450 |
110 |
90 |
Fused Magnesia (crystal size:450-600 microns)and Graphite |
VRPL MAGCARB- R5 |
97.0 |
4.0 |
4 |
11 |
3.05 |
450 |
125 |
90 |
Fused Magnesia (crystal size:450-600 microns) and Graphite |
LRF, VD, VOD slag zone |
VRPL MAGCARB- R5(S) |
97.5 |
4.0 |
3 |
10 |
3.05 |
500 |
150 |
100 |
Fused Magnesia (crystal size:450-600 microns) and Graphite |
VRPL MAGCARB- R10 |
97.0 |
8.0 |
5 |
12 |
3.00 |
450 |
125 |
90 |
Fused Magnesia (crystal size:450-600 microns) and Graphite |
VRPL MAGCARB- R10(S) |
97.5 |
8.0 |
4 |
11 |
3.00 |
500 |
150 |
100 |
Fused Magnesia (crystal size:450-600 microns) and Graphite |
VRPL MAGCARB -R15 |
97.0 |
13.0 |
5 |
13 |
2.95 |
400 |
100 |
90 |
Fused Magnesia (crystal size:450-600 microns) and Graphite |
VRPL MAGCARB- R15(S) |
97.5 |
13.0 |
5 |
12 |
2.95 |
450 |
125 |
100 |
Fused Magnesia (crystal size:450-600 microns and Graphite |
VRPL MAGCARB- SSL5 |
96.0 |
4.0 |
5 |
13 |
3.00 |
450 |
|
|
Fused magnesia,Dead Burnt magnesia and Graphite |
LRF,VD,VOD metal zone and bottom |